| Appearance | Milky white liquid |
|
| Non-volatile matter (%) | 45±1 | GB/T 1725-2007 |
| Viscosity (mPa·S) | 500-4500 | GB/T 21059-2007 |
| PH | 7.5~8.5 | GB/T 9724-2007 |
| hydroxyl value(%) | 3.9 | Based on solids |
The viscosity of the product is affected by the pH value, as the pH value increases, the viscosity and thixotropy will increase.
Application
When used with water-based isocyanate curing agent, the curing agent needs to be diluted to 60-70% with a suitable co-solvent such as PGDA or PMA+DBE (1:2) before use. At the same time, the main agent and curing agent need to be fully stirred after mixing. The ideal mixing method is to mix with a pneumatic or electric stirrer, and then dilute with water. It is generally recommended to dilute with water at 5~25% of the main agent.
It has excellent wettability and can be used in grinding, but attention should be paid to the grinding time (<2h) and grinding temperature (<50℃). There are many unstable factors in the grinding process, which may lead to decreased stability.
With a group of curing agents produced by our company, the measured paint film properties are as follows:
| Test Item | Test Data |
| Gloss (20°/60°) | 88.2 / 95.4 |
| Pencil Hardness (500g) | H (no marring) |
| Impact Resistance (Direct/Reverse) | >50 kg·cm |
| Pot Life (35°C) | 4 h |
| Water Resistance (23°C) | 240 h |
| 5% H₂SO₄ Resistance | 240 h |
| 5% NaOH Resistance | 120 h (recoverable) |
| QUV Accelerated Weathering | 1500 h, ΔE<1, Gloss loss <15% |
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.